Untuk pengelasan konstruksi menengah (kelas 50kgf/mm2, baja ST.52).
Jenis salutannya: Low Hydrogen. YP: 67.3kgf/mm2, TS: 71.3kgf/mm2, Elongation: 25%, CIV (-30degressC): 10.2kgf-m.
Kekuatan mekanik, X-ray dan ketangguhan sangat baik sehingga cocok sekali untuk pengelasan baja karbon, baja paduan rendah, tangki minyak, dan ketel uap.
Arus: AC, DC+
NIKKO STEEL Kawat Las Baja Kekuatan Tinggi RD-360 2.6mm 1pack(5kg)
Rp259.900
Persediaan
Spesifikasi Produk
| Model Number | RD-360 |
|---|---|
| Unit | 1pack(5kg) |
| Diameter (mm) | 2.6 |
| Certifications | AWS A5.1 E7016, JIS Z 3212 D5016 |
| Current | AC, DC+ |
| Yield Point (kgf/mm²) | 61.0 |
| Tensile Strength (kgf/mm²) | 66.2 |
| Elongation (%) | 28 |
| Charpy Impact Value (kgf-m) | '8.1 at 0°C |
| Berat (Kg) | 5.0 |
| Tanggal Produk Terdaftar | 31 July 2019 |
| Terakhir Diperbaharui | 27 May 2025 |
Apakah produk dengan spesifikasi yang Anda inginkan belum tersedia? Hubungi tim Layanan Pelanggan kami di sini
Informasi Produk
Deskripsi
Description
The design emphasis of the chemically basic flux is engineered to ensure the
optimum weld metal properties demanded by the specification are fully met.
The basic flux containing the appropriate alloying elements but minimal iron
powder, is extruded onto a high purity ferritic core wire and bound with a blend of
silicates that ensure both coating strength and a coating resistant to subsequent
moisture absorption.
optimum weld metal properties demanded by the specification are fully met.
The basic flux containing the appropriate alloying elements but minimal iron
powder, is extruded onto a high purity ferritic core wire and bound with a blend of
silicates that ensure both coating strength and a coating resistant to subsequent
moisture absorption.
Feature
The chemical nature of the flux together with its controlled coating factor allowsthe electrode to be used at relatively low amps. This factor together with the fairly
fluid but quick freezing slag facilitate vertical up welding including controlled
penetration root runs.
Overall the arc is very stable, slag detachability is good, fillet welds are slightly
convex and metal recovery is some 98% with respect to weight of the core wire.
Use
Medium and high tensile carbon-manganese steels with UTS of up to 510 N/mm2\nmax.\nTypical grades are :\nBS 1449 plate and sheet#cm# BS 4360 grades 43A and 43C#cm# Lloyds A & D ship steel#cm#\nBS 4360 grade 50B#cm# Lloyds grades AH and DH#cm# BS 3059 and BS 3601 grade\n320-410 API 5L A-B and X42#cm# BS 4360-50B-50C-50D#cm# BS 1501-151 430-490#cm# BS\n3602-410-460.\nSuch steels are used in ship construction#cm# bridge building and pressure vessel\nwork as well as general construction work.
GRATIS ONGKIR* ke Jabodetabek, Banten,
Jabar, & Jatim dengan minimum pembelian
Rp200.000. Lihat selengkapnya
Jabar, & Jatim dengan minimum pembelian
Rp200.000. Lihat selengkapnya
Pilih jenis produk yang diinginkan
| Nomor SKU | Model Number | Masa Persiapan Barang | Harga | Jumlah |
|---|---|---|---|---|
| Loading... | ||||
Ulasan Produk
Tidak ada ulasan
Buka WhatsApp